48_TZI_Products-for-reliable-substrate-levelling_EN_5020.pdf
1 Page
69.3 KB
Download
<h1>48_TZI_Products-for-reliable-substrate-levelling_EN_5020.pdf</h1> <p>SCHOMBURG GmbH <br />Aquafinstraße 2–8 <br />D-32760 Detmold (Germany) <br />Telephone +49-5231-953-00 <br />Fax +49-5231-953-333 <br />www.schomburg.de</p> <p>Additional technical information no. 48</p> <p>Products for reliable substrate levelling <br />ASODUR-LE</p> <p>ASODUR-EMB</p> <p>ASODUR-EV200</p> <p>ASOCRET-VK100</p> <p>ASO-SEM</p> <p>ASO-SEB</p> <p>SOLOPLAN-30-PLUS</p> <p>SOLOCRET-50</p> <p>ASOCRET-M30</p> <p>Lightweight epoxy <br />resin screed</p> <p>Epoxy resin mortar</p> <p>High performance <br />epoxy resin grouting <br />mortar</p> <p>Cement-based grouting <br />mortar</p> <p>Cement-based <br />fast setting screed <br />mortar</p> <p>Cement-based <br />fast setting screed <br />binder</p> <p>Cement-based levelling <br />compound</p> <p>Cement-based <br />levelling compound, <br />wall/floor</p> <p>Water-repellent cementbased multi-mortar</p> <p>Laying substrate on <br />wood and wooden <br />floorboards as a <br />light load distribution <br />layer</p> <p>High-strength repair of <br />cement-based surfaces <br />and covings</p> <p>Machine foundation, <br />anchor and drain <br />channel grouting, highstrength load distribution <br />layer, Dresden <br />Combibord adhesive</p> <p>Grouting of machine <br />foundations, nozzles, <br />pre-cast concrete <br />components, channels</p> <p>Dry mortar for <br />the production <br />of cement-based <br />screeds with fresh <br />in fresh tile laying</p> <p>Binder for <br />manufacture of <br />cement-based <br />screeds, quickly <br />ready to receive <br />tiles</p> <p>Fibre reinforced flow putty <br />for smoothing, filling and <br />levelling</p> <p>Non slump wall and <br />floor filler, rapid <br />setting</p> <p>Non slump levelling mortar <br />for the levelling and repair <br />of voids and damaged <br />areas and as a barrier <br />plaster</p> <p>DIN EN 13813</p> <p>DIN EN 18313</p> <p>DIN EN 13813 <br />DIN EN 1504-6</p> <p>DIN EN 13813</p> <p>DIN EN 13813</p> <p>DIN EN 13813</p> <p>DIN EN 13813</p> <p>DIN EN 998-1:2010-12 <br />DIN EN-1504-3</p> <p>EMICODE/AgBB/VOC</p> <p>Yes</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>Yes</p> <p>No</p> <p>No</p> <p>Outdoor application</p> <p>No</p> <p>Yes</p> <p>Yes</p> <p>Yes</p> <p>Yes with AIV</p> <p>Yes with AIV</p> <p>Yes with AIV</p> <p>Yes with AIV</p> <p>Yes</p> <p>E</p> <p>E</p> <p>3-75 mm B <br />> 75 mm E</p> <p>A1</p> <p>A1</p> <p>not determined</p> <p>E</p> <p>A1</p> <p>A1</p> <p>Layer thickness min/mm</p> <p>15</p> <p>2</p> <p>10</p> <p>20</p> <p>10</p> <p>10</p> <p>2</p> <p>2</p> <p>3</p> <p>Layer thickness max/mm</p> <p>not determined</p> <p>50 (100 punctual)</p> <p>200</p> <p>100</p> <p>60</p> <p>60</p> <p>30</p> <p>50</p> <p>30</p> <p>Description</p> <p>Typical area of application</p> <p>CE labelling</p> <p>Fire class</p> <p>Watertight up to</p> <p>No</p> <p>20 mm (3 bar)</p> <p>20 mm (5 bar)</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>10 mm (negative pressure)</p> <p>Low dust</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>Yes</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>Self-levelling</p> <p>No</p> <p>No</p> <p>Yes</p> <p>Yes</p> <p>No</p> <p>No</p> <p>Yes</p> <p>No</p> <p>No</p> <p>Vertical application</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>Yes</p> <p>Yes</p> <p>Cove production</p> <p>No</p> <p>Yes</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>No</p> <p>Yes</p> <p>Yes</p> <p>Machine application</p> <p>No</p> <p>No</p> <p>Yes</p> <p>Yes</p> <p>Yes</p> <p>Yes</p> <p>Yes</p> <p>No</p> <p>Yes</p> <p>Fabric basis</p> <p>Epoxy resin</p> <p>Epoxy resin</p> <p>Epoxy resin</p> <p>Cement</p> <p>Cement</p> <p>Cement</p> <p>Cement</p> <p>Cement</p> <p>Cement</p> <p>Application time (*¹)</p> <p>45 min.</p> <p>60 min.</p> <p>100 min.</p> <p>60 min.</p> <p>45 min.</p> <p>45 min.</p> <p>35 min.</p> <p>30 min.</p> <p>30 min.</p> <p>Overcoat after approx. (*¹)</p> <p>16 hrs.</p> <p>12 hrs.</p> <p>12 hrs.</p> <p>24 hrs.</p> <p>24 hrs.</p> <p>24 hrs.</p> <p>10 hrs.</p> <p>3-4 hrs.</p> <p>3 hrs.</p> <p>7 days</p> <p>7 days</p> <p>7 days</p> <p>7 days</p> <p>30 N/mm2</p> <p>25 N/mm2</p> <p>20 N/mm2</p> <p>7 N/mm2</p> <p>4 N/mm2</p> <p>5 N/mm2</p> <p>1.65 kg/m2/mm</p> <p>1.50 kg/m2/mm</p> <p>1.40 kg/m2/mm</p> <p>9 months</p> <p>12 months</p> <p>12 months</p> <p>Fully cured after approx. (*¹)</p> <p>7 days</p> <p>7 days</p> <p>7 days</p> <p>7 days</p> <p>7 days</p> <p>Compressive strength approx.</p> <p>30 N/mm2</p> <p>100 N/mm2</p> <p>109 N/mm2</p> <p>80 N/mm2</p> <p>40 N/mm2</p> <p>Flexural strength approx.</p> <p>10 N/mm2</p> <p>50 N/mm2</p> <p>40 N/mm2</p> <p>11 N/mm2</p> <p>6 N/mm2</p> <p>1.18 kg/m2/mm</p> <p>1.90 kg/m2/mm</p> <p>1.90 kg/m2/mm</p> <p>2.00 kg/m2/mm</p> <p>2.00 kg/m2/mm</p> <p>Depending on <br />aggregate and <br />mixing ratio</p> <p>18 months</p> <p>18 months</p> <p>24 months</p> <p>12 months</p> <p>12 months</p> <p>6 months</p> <p>Consumption approx. <br />Shelf life min. (*²)</p> <p>*¹ at 23°C and 50% relative humidity *² cool and dry, in original unopened container</p> <p>DT/HS/Tet/SE/LiW 50/20</p>