MONOFLEX-M_engl_1912.pdf
3 页数
316.2 KB
Download
<h1>MONOFLEX-M_engl_1912.pdf</h1> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstrasse 2– 8 <br />D-32760 Detmold - Germany <br />phone + 49-5231- 953-00 <br />fax <br />+ 49-5231- 953-108 <br />mail export@schomburg.de <br />www.schomburg.de/en</p> <p>Technical Data Sheet</p> <p>MONOFLEX-M</p> <p>Special white adhesive with elevated flexibility and high <br />synthetic resin content – frost-resistant non-slip</p> <p>Year: 04</p> <p>SCHOMBURG GmbH & Co. KG <br />Aquafinstr. 2–8 <br />D-32760 Detmold (Germany) <br />EN 12004 <br />MONOFLEX-M WEISS <br />Cementitious adhesive</p> <p>Internal and external floors or walls <br />List of characteristics</p> <p>Declared Values</p> <p>Test methods</p> <p>Adhesive force</p> <p>Initial shear adhesion: <br />Type C2 of EN 12004</p> <p>EN 1348 section 8.2</p> <p>Wetting action of water</p> <p>Shear adhesion following <br />immersion in water: <br />Type C2 of EN 12004</p> <p>EN 1348 section 8.3</p> <p>Action of climatic-thermal <br />ageing</p> <p>Shear adhesion following <br />thermal ageing: <br />Type C2 of EN 12004</p> <p>EN 1348 section 8.4</p> <p>Freeze-thawing cycles</p> <p>Shear adhesion following <br />freeze-thawing cycles: <br />Type C2 of EN 12004</p> <p>EN 1348 section 8.5</p> <p>Description: <br />MONOFLEX-M is a thixotropic powder adhesive made <br />up by cement, aggregate with selected granulometry, <br />synthetic resins and special additives. <br />MONOFLEX-M has been conceived and developed <br />for quick and sure laying of almost all types of ceramic <br />materials also onto non-absorbing substrates, or <br />onto substrates that are subject to slight dimensional <br />variations. Besides, the high resistance to vertical <br />slippage allows tiling from the top down.</p> <p> <br /> <br />Inflammable: <br /> <br />Mixing ratio: <br /> <br /> <br />Application <br />temperature: <br /> <br />Pot life: <br />Open time: <br /> <br /> <br />Ready for grouting on <br />dry supports: <br /> <br />Final hardening on dry <br />substrates: <br /> </p> <p>suggest to adapt appropriate <br />protections. <br />no <br />26 parts water to 100 parts <br />powder by weight <br />from +5° C to +40° C <br />3 hours <br />20 minutes at +23° C and <br />50% R.H. <br />24 hours at +23° C <br />14 days</p> <p>Primary Uses: <br />MONOFLEX-M can be used for: <br />• laying porcelain tiles and non-absorbing ceramic tiles. <br />• interior or exterior laying of floor and wall ceramic <br />tiles of all types even onto heated floors (hot water <br />and electric radiant floor): <br />- interior: largest size of the tiles 90 x 90 cm. For wall <br />coverings and heated floors largest size of the tiles <br />60 x 60 cm. <br />- exterior: largest size of the tiles 60 x 60 cm. For <br />wall coverings the water absorption of the tiles must <br />be less than 0.5%.</p> <p>Technical properties <br /> <br />Value <br />Requirement <br />Initial adhesion after <br />28 days: <br />≥ 1 N/mm <br />≥ 1 N/mm <br />Adhesion strenght after <br />heat ageing (14 days + <br />14 days at +70° C): <br />≥ 1 N/mm <br />≥ 1 N/mm <br />Adhesion strenght after <br />water immersion (7 days + <br />21 days into the water): ≥ 1 N/mm <br />≥ 1 N/mm <br />Adhesion after freezethaw cycle (25 cycles): ≥ 1 N/mm <br />≥ 1 N/mm <br />Flexibility (EN 12002): ≥ 2.5 N/mm <br />Flexural strength: <br /> 3 N/mm <br />Compression strength: 12 N/mm <br />Shearing strength: <br /> <br />1.4 N/mm <br />Resistance to <br />temperature: <br /> <br />from -30° C to +80° C <br />In compliance with: EN 1 2004 class C2TE <br /> <br />EN 12002 class S</p> <p>Typical Properties: <br /> <br />Consistency: <br />Colour: <br />Danger of toxicity: <br /> <br /> <br /> </p> <p>Application Procedures: <br />Surface Preparation: <br />Substrates should be free from dirt, paint, grease or <br />wax. For laying on old floors of ceramic tiles, gres, <br />marble or similar materials, it is necessary to ensure that <br />these are properly fixed to the substrate, washed and <br />degreased. It is indispensable always to leave a joint <br />of at least 3 mm between tiles. For laying wall tiles it is</p> <p> SOLOFLEX-M + water <br />very doughy <br />white and grey <br />no <br />The cement content of the <br />product may cause irritation <br />to the skin and eyes. We</p> <p>2 </p> <p>2</p> <p>2 </p> <p>2</p> <p>2 </p> <p>2</p> <p>2 </p> <p>2</p> <p>2</p> <p>2</p> <p>2</p> <p>2</p> <p>necessary to respect the expansion joints of the structure, <br />the joints between wall and wall and between wall <br />and floor; which should be filled up elastically. Leave <br />movement joints or joints on the perimeter approx. every <br />20 m2. <br />Mixing: <br />Mix MONOFLEX-M with 26% of water (pour the <br />powder in the water and not vice versa) until you obtain <br />a homogeneous, bright, plastic adhesive. Leave it rest <br />for 5 minutes, and then remix rapidly. MONOFLEX-M <br />must be used within the pot life of 3 hours. <br />Method of application: <br />Tiling: <br />INTERIOR: Lay the tiles while exerting a good pressure <br />on the tiles surface, so that contact between tile and <br />adhesive will be at least remove of 80% of their surface <br />for wall coverings and of 95-100% for floor. <br />EXTERIOR: The contact between tile and adhesive must <br />be 95-100% so to avoid the eventual rain infiltrations <br />that in case of frost could cause the detachment of the <br />tiles. Therefore, it is suggested to spread also a layer of <br />MONOFLEX-M on the back of the tiles. <br />Same procedure is recommended indoors for: <br />• floor tiles largest than 500 cm2 with water absorption <br />of the tiles ≥ 0.5% (e.g. porcelain tiles). <br />• floor tiles largest than 1100 cm2 with all the other <br />types of tiles <br />•w <br /> all tiles largest than 120 cm2 with water absorption <br />of the tiles ≥ 0.5% (e.g. porcelain tiles). <br />•w <br /> all tiles largest than 500 cm2 with all the other types <br />of tiles. <br />• s pecial applications such as industrial refrigerators, <br />basins, swimming pools, etc. <br />At +23° C and 50% of relative humidity the open time <br />is of about 20 minutes. Under unfavourable conditions <br />these time intervals can be reduced notably, therefore it <br />is important to spread the adhesive gradually, using little <br />quantities every time, and to verify often that it hasn‘t <br />formed a superficial film before tiling. To improve the <br />workability especially during the summer, it is useful to</p> <p>damp the working place and to eliminate the eventual <br />currents of air. During the first 48 hours following the <br />laying, the adhesive cannot stand the frost. The floors <br />laid with MONOFLEX-M can be open to foot-traffic <br />cautiously after about 24 hours and for grouting after <br />48 hours (at temperatures below to +15° C) They are <br />ready for normal traffic after 14 days. <br />Cleaning and Equipment Maintenance: <br />The cleaning of the coating of MONOFLEX-M must be <br />effected by means of a damp cloth or sponge when the <br />adhesive has already started to set and it can be done <br />using greater quantity of water only after 48 hours from <br />tiling. <br />Estimating and Supply: <br />Packaging: <br />MONOFLEX-M is available in 25 kg poly-lined bags <br />and 1,125 kg euro pallets loads. <br />Consumption: <br />It depends on the substrate and the type of trowel used. <br />For smooth substrate and adhesive thickness of 5-6 mm, <br />the coverage of MONOFLEX-M is 4-5 kg per m2 and it <br />increases to 0,5-1 kg per m2 for rough substrates. <br />Storage & shelf Life: <br />MONOFLEX-M must be stored in the original unopened <br />packaging in a dry and cool place. <br />White version: <br />12 months from the date listed on the package; in <br />conformity with the directive 2003/53/CE informing <br />that this time expiration regards the efficiency of the <br />reducing agent in respect to hydro-soluble chrome VI. <br />UNIFLEX-F: 6 months. <br />Grey version: <br />12 months from the date listed on the package; in <br />conformity with the directive 2003/53/CE informing <br />that this time expiration regards the efficiency of the <br />reducing agent in respect to hydro-soluble chrome VI. <br />UNIFLEX-F: 6 months.</p> <p>Health & safety: <br />Please adhere to valid European Material <br />Safety Data Sheet. <br />Advice: <br />The information given in this chart is based on our best <br />experience and indicative only. It must in any event <br />be verified by the end user, who assumes all liabilities <br />deriving from the use of the product.</p> <p>This technical data sheet does not consider local building codes or legal requirements. It shall be used as general reference for the product, based on our current knowledge <br />and experience. Legally binding is only the latest Data Sheet from one of our foreign subsidaries inside their sales territory. In any case of uncertainty please consult our <br />technical department for further information. <br />19/12 AI/JD</p>
